Electrophoretic coating for auto parts industry
Product Introduction
HL-1607LB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below:
The bath has strong anti-shrink age andanti-pollutionability.
Coating fullness of good,better sub strate hiding.
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
The appearance of the coating is flat, delicate, smooth, uniform high gloss.
Main ingredients
| Matrix resin: | Acrylic modified epoxy resin |
| Pigment: | carbon black, kaolin, antirust pigment |
| Additives | surface active agent, prevent shrinkage cavity agent |
Product quality data
| Project | Technical data | Test standard |
Resin
(HL-1607LB) | Black Paste (HLS-1701A) |
| Appearance | —— | Milky white liquid | Black viscous liquid,no agglomeration | Visual |
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1400±600 | —— | HG/T 3334 |
| Storage stability |
No stratified state, and there were no obvious difference compared to before storage | In 5-35 ℃ temperature 1 year |
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Product film performance
| Project | Indicator | Test standard |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 72 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 72 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 1000 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Customer production site:
Product Tags:
|
|
Auto Parts Industrial ED Paint Low Curing Temperature Good Salt Spray Resistance Images
|